JT-214Z Water-based Micaceous Iron Epoxy Intermediate Coating

JT-214Z Water-based Micaceous Iron Epoxy Intermediate Coating

JT-214Z Water-based Micaceous Iron Epoxy Intermediate Coating

JT-214Z Water-based Micaceous Iron Epoxy Intermediate Coating

Model : JT-214Z
Certification : ISO9001, ISO14001, ISO45001
Packaging : 22 kg/drum
Brand : JOINTAS
Place : Guangzhou, China
JT-214Z is a new environment-friendly anticorrosion coating. It’s made from water-based two-component epoxy resin, micaceous iron oxide, amine curing agent, nano-functional materials, anti-rust pigment, corrosion inhibitor, and related additives. It’s non-solvent. Anti-rust pigment with high heavy metal content, such as chromium and lead, isn’t added.

Standard: HG/T 5176-2017
Get a Quote
Product manual
JT-214Z is a new environment-friendly anticorrosion coating. It’s made from water-based two-component epoxy resin, micaceous iron oxide, amine curing agent, nano-functional materials, anti-rust pigment, corrosion inhibitor, and related additives. It’s non-solvent. Anti-rust pigment with high heavy metal content, such as chromium and lead, isn’t added.
Product feature
  • Low VOC, no pollution while construction, not flammable or explosive, safety for transportation and storage.
  • Good interlayer adhesion with primer and top coating
  • Good sealing property of the coating film, which endows the matching coating with excellent anti-corrosion performance
  • Long application period
Main purpose
As the intermediate coating of multiple anti-corrosion systems, JT-214Z is usually matched with zinc-rich primer or epoxy primer, used for anti-corrosion of various large-scale steel structures and mechanical equipment, and improve the anti-corrosion performance in various corrosive environments.
Standards compliant
HG/T 5176-2017
Technical parameters
Items Result
Luster Matte
Color Medium Grey
Mass solid content/% About 60
Volume solid content/% About 46
Specific weight About 1.35kg/L
Theoretical coating rate 6.9 m2/kg (measured as a 50-micron dry film)
Adhesion Grade 1
VOCs ≤50g/L
Tack free time ≤1h(25℃, humidity 50%)
Complete dry time ≤8h(25℃, humidity 50%)
Complete curing time 7d(25℃, humidity 50%)
Application period 6h(25℃)
Recoating time Minimum 6h, maximum 48h(25℃)
Impact resistance 50cm
Flexibility 1mm

Related Links

acrylic sealant silicone sealant gutter sealant grout sealant bathroom sealant pu foam gap filler silicone adhesive silicone caulk construction adhesive construction sealant windows sealant weather sealant silicone structural ms sealant pu sealant polyurethane sealant interior paint waterborne coatings industrial paint anti corrosion paint anti corrosion coatings house paint insulating glass sealant water-based coating for steel structure