JT-403M Water-Based High Gloss Acrylic Top Coating

Model : JT-403M
Certification : ISO9001, ISO14001, ISO45001
Packaging : 20 kg/drum
Brand : JOINTAS
Place : Guangzhou, China


JT-403M is formulated with water-based modified acrylic emulsion as the film-forming base material and added with antirust slurry, anti-rust agent, nano functional additives and other materials. Anti-rust pigment with high heavy metal content, such as chromium and lead, isn’t added.
Product manual
JT-403M is formulated with water-based modified acrylic emulsion as the film-forming base material and added with antirust slurry, anti-rust agent, nano functional additives and other materials. Anti-rust pigment with high heavy metal content, such as chromium and lead, isn’t added.
Product feature
  • Excellent anti-corrosion, anti-rust performance and initial water resistance
  • Excellent substrate adhesion, especially for carbon steel surface
  • Low VOCs content, environmental-friendly, safe and healthy
  • Good for construction
  • Excellent anti-sagging performance
Main purpose
Used in conjunction with a suitable water-based primer, JT-403M is mainly used as anti-corrosion and decorative purpose for the surface of metal such as construction machinery, port equipment, indoor and outdoor machinery. JT-403M has very good luster and hardness, excellent outdoor weather resistance. At the same time, it can also be used as anticorrosion purpose of metal surfaces such as large indoor and outdoor steel structure buildings, stadiums, bridges, petrochemical oil tanks, etc., which require high weather resistance and anti-corrosion performance.
Technical parameters
Items Result
Lustre High gloss (60-90cent) 60°
Color Various, customized as color card
Volume solid content/% About 37
Theoretical coating rate 7m2/kg (measured as a 40-micron dry film)
Specific weight About 1.15kg/L
Hardness HB
Tack free time 15℃≤1.5h, 25℃≤0.7h, 35℃≤0.4h
Complete dry time 15℃≤24h, 25℃≤12h, 35℃≤6h
Recoating time Minimum 4h, maximum 48h(25℃)
Complete curing time 7d(25℃, humidity 50%)
Adhesion Level 1
Impact resistance 50kg·cm