antas-165 Two-Component Silicone Sealant for Insulating Glass

antas-165 Two-Component Silicone Sealant for Insulating Glass (IGU)

antas-165 Two-Component Silicone Sealant for Insulating Glass (IGU)

Packaging : A+B: 189L+19L; 19L+1.9L

Brand : antas

antas-165 is two-component, non-structural, neutral-curing sealant for insulating glass. It is used as the secondary sealing in an insulating glass unit. It has good adhesion to most building materials without corrosion or stain to metal, glass, concrete, marble and etc. It has excellent weathering performance with over 15 years’ service life-time under general environment.

Get a Quote

Product feature

1. The curing speed can be adjusted. It is suitable for continuous processing for both automatic and manual production lines with fast curing speed.
2. Neutral curing with no corrosion to metal, coated glass or other building materials.
3. Good weathering performance in the resistant to ozone and UV radiation.
4. Excellent performance within broad temperature range. The cured sealant will not turn brittle, hardened or cracked at -50º C. It will not turn soft or deteriorated, but will keep good strength and flexibility at 150º C.
5. Good compatibility with other neutral silicone sealants.

Main purpose

1. Structural bonding of glass curtain wall.
2. Structural bonding of other curtain walls.
3. Bonding for industrial purpose or other buildings.
4. Secondary sealing of insulating glass.

Standards compliant

EN1279:2018
EN15434:2006+A1:2010
GB/T29755-2013

Technical parameters

Number	Test items			Measured value
1	Appearance			Even, exquisite paste, No bubble, no skinning, no gel
2	Density	Part A		1.47 g/cm³
		Part B		1.03 g/cm³
3	Sag degree		Horizontal，mm，	No deformation
			Verticality，mm，	0
4	Tack free time，h			2
5	Applicable period			49 min
6	Hardness, Shore A			40
7	Elasticity recovery rate			93%
8	Tensile adhesion	Tensile strength		0.69MPa
		Elongation at largest tensile strength		76%
		Damage area of bonding		0%
9	Adhesion at constant load			No destruction
10	Tensile adhesion after water & UV-radiation	Tensile strength		0.53MPa
		Elongation at largest tensile strength		216%
		Damage area of bonding		0%
11	Tensile adhesion after hot-air aging	Tensile strength		0.85MPa
		Elongation at largest tensile strength		87%
		Damage area of bonding		0%
12	Mass loss rate			1.3%
13	Moisture vapor transmission rate （GB 29755-2013）			11.32 g/(m2·d)
14	Moisture vapor transmission rate （EN 1279-4:2018）			12.0 g/(m2·d)

Use restrictions

Antas-165 silicone sealant for insulating glass should not be applied:
1. As the primary or single seal in an insulating glass unit.
2. In structural glazing applications.
3. In totally confined spaces.
4. On the surface of substrate that bleeds oil, plasticizer or solvent and so on(such as impregnated wood).
5. In contact with or exposed to sealants that liberate acetic acid.
6. In continuous water immersion or on the surface with fog, or wet surface, or in continuous wet place.
7. When substrate surface temperature beyond 40º C or below 10º C.
8. Surfaces in direct contact with food.

antas-165 Two-Component Silicone Sealant for Insulating Glass (IGU)

antas-165 Two-Component Silicone Sealant for Insulating Glass (IGU)

Product feature

Main purpose

Standards compliant

Technical parameters

Use restrictions