| Number | Test items | Standard Ordain | Measured value | ||
| 1 | Appearance | Even, exquisite paste, No bubble, no skinning, no gel | Even, exquisite paste, No bubble, no skinning, no gel | ||
| 2 | Sag degree | Horizontal，mm， | No deformation | No deformation | |
| Vertical，mm， | ≤3 | 0 | |||
| 3 | Extrudability, s | ≤10 | 1.4 | ||
| 4 | Tack free time，h | ≤ 3 | 1.5 | ||
| 5 | Hardness, Shore A | 20~60 | 41 | ||
| 6 | Heat deterioration | Mass loss, % | ≤10 | 4.5 | |
| Crackle | No crackle | No crackle | |||
| Powdering | No powdering | No powdering | |||
| 7 | Tensile adhesion | 23℃ | Tensile strength, MPa | ≥0.60 | 1.64 |
| Damage area of bonding, % | ≤5 | 0 | |||
| Elongation at largest tensile strength, % | ≥100 | 375 | |||
| 90℃ | Tensile strength, MPa | ≥0.45 | 0.94 | ||
| Damage area of bonding, % | ≤5 | 0 | |||
| -30℃ | Tensile strength, MPa | ≥0.45 | 2.13 | ||
| Damage area of bonding, % | ≤5 | 0 | |||
| After water immersion | Tensile strength, MPa | ≥0.45 | 1.50 | ||
| Damage area of bonding, % | ≤5 | 0 | |||
| After water & UV-radiation | Tensile strength, MPa | ≥0.45 | 1.20 | ||
| Damage area of bonding, % | ≤5 | 0 | |||
| 8 | Tensile modulus | 23℃ | Elongation is 10%, MPa | --- | 0.22 |
| Elongation is 20%, MPa | --- | 0.33 | |||
| Elongation is 40%, MPa | --- | 0.49 | |||